Copolymer of Polyamide (AK 93/7)


Copolymer Molding AK 93/7 is intended for production of constructional parts by injection molding.

Copolymer AK 93/7 is applied in machine building, electrical engineering, instrument making industries and in other spheres. It is often used as a substitute of non-ferrous metals.

Copolymer of Polyamide is resistant to hydrocarbon connections, organic solvents, oils, alkali solutions. AK 80/20 is dissolved in concentrated mineral acids, formic and acetic acids, phenols. Temperature range of operation is from-50 to +70 °C.


Properties of Polyamide AK 93/7 (GOST 19459-87)

Indicator Value
Density, g/cm³1.14
Melting temperature, °C, not lower238
Mass fraction of water, %, not more0.4
Tensile strength, MPa (kgf/cm²)
58.8 - 68.6 (600 - 700)
Critical stress at cut, MPa (kgf/cm²)49.5 - 58.8 (550 - 600)
Critical stress at compression,
MPa (kgf/cm²)
98.0 - 117.6 (1000-1200)
Brinell hardness, MPa (kgf/cm²)98.0 - 117.6 (1000-1200)
Breaking alongation, %80 - 100
Coefficient of friction against steel0.24 - 0.25
Water absorption for 24 h, %2.1 - 2.2
Water absorption, max., %9.0
Shrinkage, %1.4 - 1.8
Impact strength of a sample without
cut at 0 °C, kJ/m² (kgf·cm/cm²)
102.9 - 107.8 (105 - 110)
Impact strength of a sample without
cut at -20 °C, kJ/m² (kgf·cm/cm²)
98.0 - 107.8 (100 - 110)
Impact strength of a sample without
cut at -50 °C, kJ/m² (kgf·cm/cm²)
83.3 - 98.0 (85 - 100)
Charpy impact strength, kJ/m²
(kgf·cm/cm²), not less
3.9 (4.0)
Bending stress at specified
value, MPa (kgf/cm²), not less
71.5 (730)
Volume resistivity, Ohm·cm, not less1·10¹²
Dielectric strength, kV/mm, not less20
Dielectric loss tangent at
frequency 10⁶ Hz, not more
0.12
Combustion resistancePV-2